Hydrogen Isotope Research Center - Toyama Univ.
Data Base for Tritium Solid Breeding Materials (Li2O, Li2TiO3, Li2ZrO3 and Li4SiO4) of Fusp
5.1 Physical and thermal properties
5.1.1 Crystalline structure
No. | Data and remark | Fig. | Refs. |
1 | Monoclinic : Sintered at 1050°C, 3hr : 0.95 Li2TiO3 TD | - | 6, 50 |
Notes1 | Phase change temp. : 1150°C (β→γ) | - | - |
5.1.2 Molecular weight (g/g-mol)
No. | Data and remark | Fig. | Refs. |
1 | 109.93(11.82×10-2δ) δ=6Li fraction in Li | - | 8, 50, 51 |
5.1.3 Density and Li density (g/cm3)
No. | Data and remark | Fig. | Refs. |
1 | 3.44 (11.82×10-2δ) δ= 6Li fraction in Li | - | 8, 51 |
2 | 2.0(α), 3.43(β), 2.57(γ) : α=cubic, β=monoclinic, γ=cubic | - | 50, 51 |
Notes1 | Li density (g/cm3) : 0.37δ for 6Li , 0.44(1δ) for 7Li | - | 8 |
5.1.4 Melting point (°C)
No. | Data and remark | Fig. | Refs. |
1 | 1535°C | - | 8 |
2 | 1535°C (Li/Ti = 2.0, 100%TD) | - | 51 |
5.1.5 Thermal conductivity (W/m-K)
No. | Data and remark | Fig. | Refs. |
1 | 2 (1000K, 85%TD) | - | 6 |
2 | 1.955 (Li/Ti = 1.9, 80%TD, 500°C) | - | 51 |
3 | 3.258(12p) monoclinic, p : porosity(0.1~0.3) | - | 51 |
4 | κ=(1p)2.9(5.354.78×10-3T+2.87×10-6T2)
0.14≦p (porosity)≦0.25, 400≦T≦1400K |
- | 8, 64, 50, 52 |
5 | Pebble bed thermal conductivity, (W/m-K)
κ=(1p)[0.74+0.00015(T273)+3.3×10-7(T273)2]/0.52 0.7~1.2 mm diameter pebble, 0.1 MPa He 0.4314≦p (smear porosity)≦0.48, 300≦T≦300K |
- | 53, 6 |
Notes1 | The thermal conductivity data for Li2TiO3. | 5.1 | 27, 28, 92 |
5.1.6 Thermal expansion
No. | Data and remark | Fig. | Refs. |
1 | Linear expansion, (%), from 293K
ΔL/L0=0.4119+1.154×10-3T+5.505×10-7T2 |
- | 50 |
2 | Instantaneous coef., (1/K)
α=1.154×10-5×1.101×10-8T |
- | 50 |
3 | Mean coef., (1/K), from 293K
αm= (0.004119+1.154×10-5T+5.505×10-9T2)/(T293) 373≦T≦1073K |
- | 50 |
4 | 16×10-6 (1/K) | - | 6 |
5 | 21×10-6 (1/K, Li/Ti = 1.9, 80%TD) | - | 50 |
5.1.7 Specific heat (kJ/kg-K)
No. | Data and remark | Fig. | Refs. |
1 | Cp = 355(T100)1.1/(1+0.3 T1.05), (kJ/kg-K)
300≦T≦1400K |
- | 8, 54, 55, 28 |
2 | 1.0 kJ/kg-K, (300K) | - | 50, 52 |
Notes1 | Specific heat data for Li2TiO3. The dotted curve is fitting curve. | 5.2 | 28 |
5.1.8 Heat capacity (J/mol.-K)
No. | Data and remark | Fig. | Refs. |
1 | 1428 J/kg-K, (Li/Ti = 1.9, 80%TD, 500°C) | - | 50 |
5.1.9 Vapor pressure
No. | Data and remark | Fig. | Refs. |
1 | Temperature at which total lithium vapor pressure is 0.01 Pa, (K)
K=839+[305+87.3 log100P(D2O)]78.3 logP(D2)/[1+2.55×10-10log100P(D2O)18.6] 10≦P(D2)≦1000 Pa, 0.01≦P(D2O)≦100 Pa P(D2) : partial pressure of D2. |
- | 57, 58, 59, 60 |
5.1.10 Thermal diffusivity (10-6m2/s)
No. | Data and remark | Fig. | Refs. |
1 | α=5.16×10-7m2/s, 80%TD, 500°C, Li/Ti = 1.9
From 6.45(1p)×10-7m2/s, p : porosity |
- | 50, 28 |
2 | Measured thermal diffusivity of 80% dense Li2TiO3. | 5.3 | 92, 28 |