Data Base for Tritium Solid Breeding Materials (Li2O, Li2TiO3, Li2ZrO3 and Li4SiO4) of Fusion Reactor Blankets --- Yoshiaki FUTAMURA
6. Database for Li2ZrO3
6.3 Chemical stability and compatibility
6.3.1 Compatibility with water
No. | Data and remark | Fig. | Refs. |
1 | Interaction with water (liquid) : hydrolyses at 25°C and 100°C. | - | 12, 73, 39, 75 |
2 | Li in Li2ZrO3 is fully soluble after 1 month water immersion. | - | 12 |
3 | Water vapor solubility --- No data. | - | 12 |
4 | Water vapor adsorption --- No data. | - | - |
6.3.2 Compatibility with structural materials
No. | Data and remark | Fig. | Refs. |
1 | Interaction with steel :
No significant interaction in conditions explored : up to 700°C in vacuum. |
- | 48 |
6.3.3 Compatibility with Beryllium
No. | Data and remark | Fig. | Refs. |
1 | No significant interaction up to 650°C in vacuum.
Slight oxidation of beryllium in wet helium. |
- | 48 |
6.3.4 Compatibility with acid --- No data
6.3.5 Compatibility with reprocessing liquid --- No data