Data Base for Tritium Solid Breeding Materials (Li2O, Li2TiO3, Li2ZrO3 and Li4SiO4) of Fusion Reactor Blankets --- Yoshiaki FUTAMURA
6. Database for Li2ZrO3
6.1 Physical thermal properties
6.1.1 Crystalline structure
No. | Data and remark | Fig. | Refs. |
1 | Monoclinic < 1100°C, Cubic > 1100°C | - | 8, 6 |
Notes1 | Phase change : 1100°C | - | - |
6.1.2 Molecular weight (g/g-mol)
No. | Data and remark | Fig. | Refs. |
1 | 153.25(11.31×10-2δ) : δ=6Li fraction in Li | - | 8, 60 |
6.1.3 Density and Li density (g/cm3)
No. | Data and remark | Fig. | Refs. |
1 | 4.1573(11.31×10-2δ) : δ=6Li fraction in Li | - | 8 |
6.1.4 Melting point
No. | Data and remark | Fig. | Refs. |
1 | 1695±15°C | - | 85, 69 |
6.1.5 Thermal conductivity (W/m-K)
No. | Data and remark | Fig. | Refs. |
1 | k=(1p)5/3[3.643(1+1.549×10-3T)-1+7.579×10-10T3]
0.187≦p (porosity)≦0.211, 373≦T≦1063K |
- | 70 |
2 | κ=0.0102+6.68T-1 (W/cm-K), <670K, 78.9%TD | - | 72 |
3 | 1.8 (W/m-K), 800K, 85%TD | - | 6 |
4 | Thermal conductivity for Li2ZrO3 (80%TD). | 6.1 | 17 |
6.1.6 Thermal expansion
No. | Data and remark | Fig. | Refs. |
1 | Thermal expansion
Linear expansion, (%) : ΔL/L0 Instantaneous coef., (1/K) : α Mean coef., (1/K) : αm ΔL/L0=9.89×10-4(1+1.13×10-5T)(T298) α=9.86×10-6(1+2.27×10-5T) αm=9.89×10-6(1+1.13×10-5T) |
- | 63 |
2 | 9.99×10-6 (1/K), (Mean coef., T=898K) | - | 84 |
6.1.7 Specific heat (kJ/kg-K)
No. | Data and remark | Fig. | Refs. |
1 | Cp=1.0223.696×10-5T2.791×104T-2 : 350≦T≦1012K | - | 73 |
2 | 0.7 (kJ/kg-K), 300K | - | 6 |
6.1.8 Heat capacity (J/K-mol)
No. | Data and remark | Fig. | Refs. |
1 | Cp = 114.7+4.772×10-2+7.214×102/T2 : 350≦T≦750K | - | 72, 6 |
2 | 912 (J/kg-K) | - | 50 |
6.1.9 Vapor pressure (Pa)
No. | Data and remark | Fig. | Refs. |
1 | logP(Li)=18.39×103/T+10.69 : 1031≦T≦1642K | - | 74 |
6.1.10 Thermal diffusivity
No. | Data and remark | Fig. | Refs. |
1 | 4.94×10-7 (m2/s) at 500°C, 80%TD, Li/Zr=1.9
From 6.175(1p) at 500°C, p : porosity |
- | 50 |
2 | Thermal diffusivity of 80%TD Li2ZrO3, 80%TD Li2O and 80%TD Li4SiO4. | 6.13 | 12 |